The crux of understanding the superconducting mechanism in pressurized Ruddlesden-Popper nickelates hinges on elucidating their structural phases. Under ambient conditions, the trilayer nickelate La4Ni3O10 stabilizes in a twinned monoclinic structure with space group P21/c. Upon heating, it undergoes a structural transition to the tetragonal I4/mmm phase at Ts ~ 1030 K, while a second transition associated with the onset of density-weave (DW) ordering emerges upon cooling below TDW ~ 135 K. Here from pressure-temperature x-ray diffraction on high quality flux-grown single crystals we unequivocally demonstrate a direct tetragonal-to-monoclinic transition with no trace of intermediate orthorhombic Bmab phase. Ab initio density-functional theory calculations as a function of pressure fully corroborate the experimental observations. The transition unfolds as a 2-fold superstructure due to the emergence of commensurate superlattice reflections and can be progressively suppressed from 1030 K down to 20 K under 14 GPa. No discernible structural distortions associated with DW ordering are detected down to 20 K at ambient pressure. This is in contrast to Raman measurements that reveal the appearance of additional phonon modes below 130 K, implying a further reduction in symmetry from monoclinic P21/c and thus indicating the presence of a third structural phase associated with the DW ordering in La4Ni3O10.