#1 Maximizing solubility in rock salt high-entropy oxides [PDF] [Copy] [Kimi] [REL]

Authors: Matthew Furst, Joseph Petruska, Dhiya Srikanth, Jacob T. Sivak, Susan B. Sinnott, Christina M. Rost, Jon-Paul Maria, Saeed S. I. Almishal

To explore and quantitatively map the cation-size mismatch solubility limits in high-entropy oxides (HEOs), we report on Ca2+ substitution in prototypical MgCoNiCuZnO, because, while isovalent, Ca^{2+} is 38% larger than its partners' average ionic radii. Using the thermodynamics-grounded bond-length distribution descriptor, we identify Ca^{2+}-Cu^{2+} interactions as the primary prospective lattice destabilizer. Bulk synthesis confirms only 4% Ca solubility with Cu at 950^oC, modestly rising to 5% after Cu removal at 1150^oC. We then employ far-from-equilibrium pulsed-laser deposition to investigate metastable solubility: epitaxial films incorporate 10% Ca with Cu and a full 20% Ca without, doubling and quadrupling the respective bulk limits. This Ca uptake additionally enables deterministic lattice-parameter control via Ca concentration. Overall, our results demonstrate both the extended solubility possible in HEO systems, particularly when accessing metastable states through quenching from high-energy plasma, and that the specific constellation of solid-solvent cations can be rationally engineered to minimize bond-length distributions when largely misfit cations are added, thus expanding the accessible compositional space.

Subject: Materials Science

Publish: 2025-06-18 16:25:35 UTC