Total: 1
Ambient-pressure superconductivity in nickelates has been capped at an onset transition temperature (Tc) of ~40 K, a value that remains lower than the cuprate (~133 K) and iron-based (~55 K) counterparts, despite the promise shown under high pressure. Here, we report ambient-pressure superconductivity onset at ~63 K in epitaxial (La,Pr)3Ni2O7 thin films grown under compressive strain on SrLaAlO4 substrates. This Tc leap is enabled by pushing our gigantic-oxidative atomic-layer-by-layer epitaxy (GAE) method into an extreme non-equilibrium growth regime. It leverages powerful in situ oxidation to simultaneously enhance kinetics via higher temperatures and achieve full oxygenation without post-annealing. Synchrotron X-ray diffraction and scanning transmission electron microscopy confirm that this approach yields films of large-scale crystalline purity, overcoming the inherent metastability of the strained superconducting phase. These films exhibit a systematic evolution in their normal-state resistivity-temperature curve: the power-law exponent $α$ evolves from Fermi-liquid-like ($α$ ~2) at lower Tc to strange-metal-like ($α$ ~1) in higher Tc samples, directly linking the enhanced superconductivity to non-Fermi liquid behavior. Mapping the vortex melting phase diagram by the mutual inductance technique further reveals 2D melting limit suppressed to near zero, which demonstrates significantly stronger interlayer coupling than that of cuprates. These results identify the nickelates as an anisotropic-3D high-Tc system exhibiting strange-metal behavior, presenting an alternative framework to the quasi-2D cuprate paradigm.