Anomalous Hall effect studies were performed at 300 K on Si/Fe multilayers prepared by dc magnetron sputtering. About 60 times enhancement in the saturation Hall resistance and 80 times enhancement in anomalous Hall coefficient are obtained in [Si(50 angstrom)/Fe(tFe)]_20 multilayers when decreasing the Fe layer thickness from 100 Angstrom to 20 Angstrom. The largest anomalous Hall coefficient (Rs) of 1.4 x 10^-7 Ohm m/T was found for t_Fe=20 Angstrom, which is about three orders of magnitude larger than that of pure Fe and Fe/Cr, Al/Fe, Cu/Fe, SiO2/FePt/SiO2 multilayers. The ordinary Hall coefficient R_0 was about two orders of magnitude larger than that of pure Fe. The R_s was found to vary with the longitudinal electronic resistivity, Rho as R_s proportional to (Rho)^2.2, indicating the role of interfaces for the enhancement of the anomalous Hall effect in the multilayers. An increase of Hall sensitivity from 9 mOhm/T to 1.2 Ohm/T is observed on decreasing tFe from 100 Angstrom to 10 Angstrom. The high Hall sensitivity obtained is about three orders of magnitude larger than that of Al/Fe and Cu/Fe multilayers, showing it as an emerging candidate for Hall element for potential applications.