Total: 1
We assess the impact of atomistic substrate lattice relaxation schemes in the primary band gap at charge neutrality and the secondary valence band gap of graphene on hexagonal boron nitride (G/h-BN) as a function of twist angle. For zero twist angle, the primary gap decreases from $\sim 30$~meV in fully relaxed suspended G/h-BN bilayers, to $\sim 9$~meV when the remote h-BN substrate layer is kept rigid, and down to $\sim 3$~meV in completely rigid structures. In the presence of relaxations, the primary gap shows a maximum near $\sim 0.6^{\circ}$ coinciding with energetic stabilization due to alignment between the moiré pattern and the graphene lattice vectors, while the secondary valence band gap drops from $\sim 12$~meV down to zero beyond twist angles of $\sim 1^{\circ}$. A small but finite primary gap on the order of $\sim 1$~meV, with a mass sign favoring electronic occupation of carbon atop boron, persists across twist angles from $0^{\circ}$ to $30^{\circ}$ for all sliding configurations, and switches sign for twist angles between $30^{\circ}$ and $60^{\circ}$.