Freestanding GdBa2Cu3O7 (GdBCO) superconducting thin films were fabricated using a water-soluble Sr3Al2O6 (SAO) sacrificial layer in combination with thermal release tape. An amorphous Al2O3 capping layer was introduced to suppress crack formation during the lift-off process. The influence of buffer-layer design inserted between the GdBCO and SAO layers was systematically investigated with respect to structural integrity and superconducting properties after lift-off. A LaAlO3/SrTiO3 bilayer buffer was found to be essential for maintaining epitaxial growth and a superconducting transition temperature (Tc) of approximately 92 K after lift-off, comparable to that of the as-grown films. In contrast, a reversed SrTiO3/LaAlO3 bilayer and single-layer buffer structures led to a suppression of Tc, highlighting the critical role of stacking sequence. These results demonstrate that optimization of the buffer-layer design is a key factor for realizing high-quality freestanding GdBCO films while maintaining their superconducting characteristics.