Superconductivity in the Ruddlesden-Popper (RP) nickelates has so far been confined either to multilayer compounds under high pressure or to square-planar infinite-layer-type films stabilized by epitaxial strain. Here we report the high-pressure high-temperature (HPHT) growth of bulk single crystals of the quadruple-layer RP nickelate La$_5$Ni$_4$O$_{13}$ ($n=4$) and reproduce the quintuple-layer La$_6$Ni$_5$O$_{16}$ ($n=5$) synthesis, two members of the series that had previously been accessible only as thin films. Topotactic reduction of La$_5$Ni$_4$O$_{13}$ single crystals with CaH$_2$ yields the square-planar phase La$_5$Ni$_4$O$_{10}$, which we show to be a bulk, ambient-pressure superconductor with $T_\mathrm{c}^\mathrm{onset} \approx 18\,\mathrm{K}$, a shielding fraction above 60\%, and a specific-heat jump that confirms a bulk pairing transition. All crystals show besides superconductivity a coexistence with a density-wave or metal-insulator transition. The upper critical field shows a small anisotropy, $γ\approx 2.4$, which remains finite as $T \to T_c$, indicating three-dimensional superconductivity with substantial coupling between the four-layer blocks. These results identify the square-planar nickelates $R_{n+1}$Ni$_n$O$_{2n+2}$ as a bulk platform in which the layer number alone tunes the nickel valence into the superconducting regime, without chemical substitution, pressure, or epitaxial constraint.