#1 Room temperature Multiferroicity and Magnetoelectric coupling in (1-x) BaTiO3-(x) CaMnO3 solid solution [PDF] [Copy] [Kimi] [REL]

Authors: P. Maneesha ; Koyal Suman Samantaray ; Rakhi Saha ; Rajashri Urkude ; Biplab Ghosh ; Arjun K Pathak ; Indranil Bhaumik ; Abdelkrim Mekki ; Khalil Harrabi ; Somaditya Sen

Materials with magnetoelectric coupling (MEC) between ferroic orders at room temperature are extremely important in modern technology and physics. BaTiO3 is a robust ferroelectric in which several doping have led to MEC. However, often MEC depends on the amount of substitution. In a series of (1-x)BaTiO3.(x)CaMnO3 (x=0,0.03, 0.06, 0.09), MEC was only observed in (0.97)BaTiO3.(0.03)CaMnO3. The structural modifications with changing substitution reveal a reduced Ti-O-Ti angle for this sample which is the most ferromagnetic in nature. A mixed phase of tetragonal P4mm and hexagonal P63/mmc space groups of BaTiO3 is observed in the substituted samples, with nominal contribution of the hexagonal phase for x=0.03. A valence state study using XPS and XANES reveals the presence of enhanced proportion of Mn3+ ions in the sample which support a Jahn-Teller distortion, thereby supporting the ferroelectricity for x=0.03. Indirect and direct evidences of MEC was obtained from magnetodielectric and magnetoelectric measurements. A magnetocapacitance of 0.4% was observed with a dc magnetic field of 4kOe at 10kHz, while magnetoelectric coupling coefficient, {\alpha}ME ~88 mVcm-1Oe-1 was obtained for dc magnetic field of 600 Oe and a 10Hz ac field of 40 Oe. Such MEC was not observed for higher substitution which emphasizes the sensitivity of the structural properties on substitution.

Subjects: Materials Science ; Applied Physics

Publish: 2024-10-29 13:08:21 UTC