The recent discovery of high-transition temperature (Tc) superconductivity in pressurized La3Ni2O7 bulk crystals has attracted keen attention due to its characteristic energy diagram of eg orbitals, containing nearly half-filled d3z2−r2 and quarter-filled dx2−y2 orbitals. This finding provides valuable insights into the orbital contributions and interlayer interactions in double NiO6 octahedra, offering opportunities to control the electronic structure via ligand field variations. Here, we demonstrate strain-tuning of Tc over a range of 50 K in La3Ni2O7 films grown on different oxide substrates under 20 GPa. As the c/a ratio increases, the onset Tc systematically rises from 10 K in the tensile-strained film on SrTiO3 to a maximum of about 60 K in the compressively strained film on LaAlO3. These systematic variations suggest that strain engineering is a promising strategy for expanding superconductivity in bilayer nickelates by tuning the orbital energy landscape toward high-Tc superconductivity.