Alkali-metal intercalation-deintercalation (AMID) enables access to metastable layered materials such as 2$M$-WS$_2$. Mechanistic studies of AMID have focused on intercalation; how deintercalation proceeds and influences crystal properties is comparatively poorly understood. Here, we assess 34 deintercalation treatments of 2$M$-K$_x$WS$_2$ and find that K$^+$ removal proceeds through coupled redox and ion-exchange equilibria, whose positions set the composition, structure, and electronic quality of the products. Across a series of neat solvents, K$^+$ deintercalation amount increased with solvent polarity and was driven to near-completion upon addition of nonoxidizing crown ether chelators, regardless of solvent polarity. Spontaneous reintercalation occurred when 2$M$-WS$_2$ was placed in dilute aqueous solutions of the strong base KOH but not the neutral salt KCl. These results suggest that the extent of deintercalation is governed by the stability of K$^+$ in solution, rather than oxidant strength alone, consistent with a reaction under thermodynamic control. Treatments that bias the deintercalation equilibrium most strongly toward the products while avoiding deleterious side reactions produce the highest quality 2$M$-WS$_2$. A six-hour treatment with acidified K$_2$Cr$_2$O$_7$ gave the highest average residual resistivity ratio ($\overline{RRR}$). Residual K$^+$, quantified by ICP-MS, was found in all treated samples and appeared to impose an upper bound on $\overline{RRR}$. Treatments yielding crystals with $\overline{RRR}$ below this bound did not always afford 2$M$-WS$_2$; we observed two new structures in bleach-treated samples and signatures of alternative phases under other conditions. This work demonstrates that deintercalation is not merely a processing step in AMID but a mechanistically rich reaction that might be rationally tuned to improve and control metastable materials.