A series of SmFeAsO1-xFx (Sm1111) bulk samples are synthesized using an in-situ cubic-anvil high-pressure (CA-HP) technique at 4 GPa and are characterized through structural, microstructural, Raman, transport, and magnetic measurements. A systematic reduction of lattice parameters and unit-cell volume confirms effective fluorine substitution at oxygen sites, while Raman spectroscopy reveals electron doping and subtle changes in local bonding environments. In the underdoped regime, the superconducting transition temperature (Tc) is enhanced by 10-17 K and the critical current density (Jc) is increased by up to an order of magnitude. The upper critical field (Hc2), estimated using the Werthamer-Helfand-Hohenberg model, reaches ~200 T, indicating strong spin paramagnetic effects and multiband superconductivity. Resistive broadening under applied fields follows Arrhenius behavior, with the activation energy showing a power-law field dependence that decreases rapidly at higher fields, consistent with collective vortex pinning. The superconducting phase diagram constructed from Tc and Jc versus fluorine content reveals a dome-like trend, with a maximum Tc of 57 K and Jc of 10^4 A-cm^-2 at the optimal doped region. A direct comparison with CSP samples demonstrates that high-pressure synthesis simultaneously enhances both Tc and Jc across the entire fluorine-doping range. These findings establish high-pressure growth as a highly effective approach for optimizing iron-based superconductors and underscore its potential for both fundamental research and future high field applications.