Valley polarization in 2D TMDs is promising for low-power valleytronic and spin-valley information processing, but time-reversal symmetry in pristine nonmagnetic TMDs keeps the K+ and K- valleys degenerate, limiting device applications. In this work, we investigated the structural stability, electronic properties, and tunable valley polarization of V-alloyed MoTe2 monolayer, Mo0.75V0.25Te2, using first-principles density functional theory (DFT) calculations. Substitutional alloying of MoTe2 with V introduced magnetic exchange interaction, which, together with spin-orbit coupling (SOC), lifted the valley degeneracy at the unequal valleys. The alloyed structure was found to be energetically and dynamically stable due to the absence of imaginary phonon modes. In pristine MoTe2, SOC produced spin splittings of 34.0 meV and 218.9 meV in the conduction bands and valence bands, respectively, but no valley polarization was observed. In contrast, Mo0.75V0.25Te2 exhibited spontaneous valley polarization of 37.3 meV in the conduction band and 78.2 meV in the valence band. The valley polarization was further enhanced by external electric fields and biaxial strain. A transverse electric field along the crystal c axis produced the maximum valley splitting of 132.8 meV in the valence band, whereas biaxial tensile strain increased the valence band valley splitting up to 160.8 meV. The maximum conduction band valley splitting reached 54.4 meV under 2% biaxial compressive strain. These results demonstrated that V alloying, combined with electric-field and strain engineering, provides an effective strategy for achieving large and tunable valley polarization in MoTe2. Thus, Mo0.75V0.25Te2 can be considered a promising 2D platform for tunable valleytronic device applications, such as transistors and sensors.