We investigate the influence of the pelletization pressure on the structural, microstructural, and superconducting properties of fluorine-doped PrFeAsO0.7F0.3 (Pr1111). Precursor powders are pressed into pellets at pressures ranging from 174 to 1131 MPa, after which the applied pressure is released and all samples undergo an identical two-step conventional synthesis process at ambient pressure (CSP-AP). All samples predominantly exhibit the tetragonal P4/nmm structure, and the lattice parameter a and unit-cell volume V decrease with increasing pelletization pressure up to an intermediate-pressure range (~900 MPa) before increasing at higher pressures. The actual fluorine-content derived from energy-dispersive X-ray spectroscopy (EDX) also increase with pelletization pressure, while Raman spectra show only modest variations in the characteristic vibrational modes associated with Fe and As. The superconducting response exhibits a non-monotonic dependence on the pelletization pressure. Among the investigated samples, the sample pelletized at 870 MPa exhibits the most favorable overall superconducting properties, with a superconducting onset temperature of 44.2 K, ~5 K higher than that of the lowest-pressure sample. It also displays a narrower superconducting transition, the highest relative sample density, a favorable effective magnetic critical current density at high fields, and a relatively large effective thermally activated flux-flow activation energy. At higher pelletization pressures, the superconducting response deteriorates, coinciding with increases in the lattice parameters, increased secondary-phase contributions, and reduced relative density. These findings establish the pelletization pressure as a relevant processing parameter for modifying the structural, microstructural and superconducting properties of Pr1111 during CSP-AP.